Manganese-Cobalt Spinel Coating Powder

Cat No:FCSM-0030

Description

Specialized ceramic powder for thermal spray or screen printing onto SOFC interconnects to prevent chromium poisoning and enhance surface conductivity.

Datasheet

Inquiry

Basic Information

Material Composition	Mn1.5Co1.5O4 Spinel
Thickness (μm)	N/A
Density (g/cm³)	5.2
Surface Resistance (mΩ·cm²)	< 10 (Specific)
Tensile Strength (MPa)	N/A
Thermal Conductivity (W/m·K)	2.5
Porosity (%)	15 (As Layer)
Operating Temp Max (°C)	1000
Flexural Strength (MPa)	N/A
Corrosion Resistance (μA/cm²)	Excellent
Contact Angle (°)	70
Gas Permeability (cm³/cm²·s)	< 10⁻⁶
Coefficient of Thermal Expansion (10⁻⁶/K)	11.2
Shore Hardness	N/A
Ash Content (%)	100
Mean Pore Size (μm)	0.5 - 2
Compressive Strength (MPa)	N/A
Electrical Conductivity (S/cm)	60 (at 800°C)
Specific Surface Area (m²/g)	5
Young's Modulus (GPa)	N/A
Chemical Stability	Cr-Vapor Barrier
Coating Material	Spinel Oxide
Surface Roughness (Ra)	N/A