Reinforced Alkaline Anion Exchange Membrane (AEM-V2)

Cat No:FCEM-0002

Description

This membrane is engineered for alkaline fuel cells (AFCs) and water electrolyzers, providing high hydroxide ion mobility without the need for precious metal catalysts.

Datasheet

Inquiry

Basic Information

Polymer/Material Base	Quaternized Polysulfone / Polyethylene
Ion Exchange Capacity (IEC)	1.4 - 1.8 meq/g
Ionic Conductivity (S/cm)	0.07 - 0.09 (at 80°C)
Thickness (μm)	35 - 50
Tensile Strength (MPa)	55 - 70
Elongation at Break (%)	10-20
Water Uptake (%)	15 - 25
Swelling Ratio (%)	< 8
Max Operating Temp (°C)	85
Chemical Stability (Fenton’s Test)	Excellent in KOH
Density (g/cm³)	1.25
Ash Content (%)	< 0.1
Volatile Content (%)	< 2.0
EW (Equivalent Weight)	600 - 800
Glass Transition Temp (Tg)	115
Storage Humidity (%)	30 - 50
Storage Temp (°C)	10-25
Solubility in Polar Solvents	Soluble in NMP
Ionic Resistance (Ω·cm²)	0.12
Dimensional Stability (%)	< 5
Thermal Stability (TGA)	> 220°C
Flammability Rating	HB
Surface Roughness (Ra)	< 0.8 μm